Abstract
Ternary oxide glass system of chemical composition of 80B2O3–(20-x)Na2O–xCdO (where x=0, 2, 4, 6, 8, 10, 12, 14mol%) have been prepared by conventional melting and quenching method. The micro structural and morphological investigation of synthesized glass samples were carried out by using XRD, FE-SEM. The supporting physical and composition dependent properties such as experimental and theoretical density, molar volume, oxygen packing density, ionic concentration, interionic distance and polaron radius were determined. Density of glass samples increases, while molar volume decreases with the increasing cadmium oxide concentration from 0 to 14mol%. X-ray diffraction profiles and FE-SEM images confirmed amorphous nature of investigated glass samples. Elemental analysis and information about the chemical composition of glass matrices have been ascertained by using EDS spectra. The interpretation of functional groups [BO3] and [BO4] units present in the oxide glass was simulated by using deconvoluted Raman spectra and FTIR spectroscopy. BO stretching, metal cation active vibrational modes and bending vibrations of BOB linkage in borate glass network are cross verified by using FTIR and Raman spectroscopy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.