Abstract
Abstract The chemical or mechanical performance of amorphous SiO2 films depend on intrinsic physicochemical properties, which are intimately linked to atomic and molecular arrangements in the Si–O–Si network. In this context, the present work focuses on a comprehensive description of SiO2 films deposited from a well-established chemical vapor deposition process involving tetraethyl-orthosilicate, oxygen and ozone, and operating at atmospheric pressure in the range 400–550 °C. The connectivity of the silica network is improved with increasing the deposition temperature (Td) and this is attributed to the decreased content of hydrated species through dehydration-condensation mechanisms. In the same way, the critical load of delamination increases with increasing Td thanks to the silicon substrate oxidation. The utilization of a O2/O3 oxidizing atmosphere involving the oxidation of intermediates species by O2, O3 and O., allows increasing the deposition rate at moderate temperatures, while minimizing carbon, H2O and silanol contents to extremely low values (4.5 at.% of H). The SiOx stoichiometry and Td interplay reveals two distinct behaviors before and above 450 °C. The best corrosion resistance of these films to standard P-etching test is obtained for the minimum silanol content and the best network molecular ordering, with an etching rate of 4.0 ± 0.1 A/s at pH = 1.5. The elastic modulus and hardness of the films remain stable in the investigated range of deposition temperature, at 64.2 ± 1.7 and 7.4 ± 0.3 GPa respectively, thanks to the low content in silanol groups.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.