Abstract
A metal-insulator-semiconductor (MIS) structure containing an HfO2/SiO2 stack tunnel layer, isolated Germanium (Ge) nanocrystals, and an HfO2 capping layer, was obtained by an electron-beam evaporation method. A high-resolution transmission electron microscopy (HRTEM) study revealed that uniform and pronounced Ge nanocrystals had formed after annealing. Raman spectroscopy provided evidence for the formation of Ge-Ge bonds and the optimal annealing temperature for the crystallization ratio of the Ge. The electric properties of the MIS structure were characterized by capacitance-voltage (C-V) and current-voltage (I-V) measurements at room temperature. Negative photoconductivity was observed when the structure was under a forward bias, which screened the bias voltage, resulting in a decrease in the current at a given voltage and a negative shift in flat band voltage. A relatively high stored charge density of 3.27 x 10(12) cm 2 was also achieved.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.