Abstract
BaZr0.2Ti0.8O3 (BZT) relaxor ferroelectric (FE) films with tetragonal structure were deposited on Pt/TiO2/SiO2/Si(100) substrates via a sol-gel technique. A giant electrocaloric effect (ECE) was observed in the compact films with ΔT = 43.6K and ΔS = 61.9J/Kkg at near room temperature of 366.5 K, which was attributed to the high breakdown electric field of E = 1010kV/cm. Meanwhile, large negative ECE (ΔT = − 5.2 K and ΔS = − 8.8J/Kkg at room temperature of 305K, ΔT = − 5.1K and ΔS = − 7.2J/Kkg at near room temperature of 375 K) were achieved. The abnormal negative ECE is originated from structural transformation in relaxor ferroelectrics. The coexisting of giant negative and positive electrocaloric effects makes it more effective to realize the refrigeration during the application or removal of an electric field. The maximum electrocaloric coefficient (ζmax = 0.043Kcm/kV) and refrigeration efficiency (COP = 35.18) of the films were obtained at near room temperature of 366.5K. The giant electroelectric effect makes BZT films promising as lead-free materials for application in environment-friendly refrigeration equipment at near room temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.