Abstract
Nd 8 Fe 73 Co 5 Hf 2 B 12 alloys were cast as strips (thick continuous ribbons with thickness t=100–160 μm) by a chill disk melt spinning technique (vdisk=3 m/s) from a master alloy prepared by arc melting (A) and from two prealloyed components (B). Samples obtained by the B procedure revealed in the as-cast state, good magnetic properties with an unusually high value of the coercivity, Hc=10.3 kOe, for the substoichiometric Nd2Fe14B system. A high degree of structural refinement and a homogeneous dispersion of the phases are attained in sample B. The strength and type of magnetic interactions between the grains are presented by δM and irreversible susceptibility plots.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.