Abstract
A biocompatible Si 3N 4-bioglass composite was coated with nanocrystalline diamond (NCD) by the hot filament chemical vapour deposition technique (HFCVD) using a H 2/Ar/CH 4 gas mixture. The advantages of the biocomposite are combined with a hard, smooth and low friction coating, making it a potential material for biotribological applications. Very low intrinsic surface roughness in the range 5 to 15 nm was determined by AFM and crystallite sizes of 1 to 30 nm were measured by TEM. The substrate temperature, Ar / H 2 ratio, starting roughness and cooling rate after deposition are key factors in determining the uniformity and adhesion of the NCD film to the biocomposite. To avoid blistering and guarantee high adhesion levels, depositions must be conducted below the bioglass crystallization temperature (637 °C). The highest growth rate (1 μm h − 1 ) was reached with a Ar / H 2 = 0.1 ratio. Brale indentation tests with 200 N showed that flat lapped substrates give a better adhesion relatively to smoother ones pre-polished in soft cloths. Slow cooling rates after deposition (2 °C min − 1 ) prevented film delamination under this applied load.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.