Natural polyphenols enhance stability of crosslinked UHMWPE for joint implants.

Abstract

Radiation-crosslinked UHMWPE has been used for joint implants since the 1990s. Postirradiation remelting enhances oxidative stability, but with some loss in strength and toughness. Vitamin E-stabilized crosslinked UHMWPE has shown improved strength and stability as compared with irradiated and remelted UHMWPE. With more active phenolic hydroxyl groups, natural polyphenols are widely used in the food and pharmaceutical industries as potent stabilizers and could be useful for oxidative stability in crosslinked UHMWPE. We asked whether UHMWPE blended with polyphenols would (1) show higher oxidation resistance after radiation crosslinking; (2) preserve the mechanical properties of UHMWPE after accelerated aging; and (3) alter the wear resistance of radiation-crosslinked UHMWPE. The polyphenols, gallic acid and dodecyl gallate, were blended with medical-grade UHMWPE followed by consolidation and electron beam irradiation at 100 kGy. Radiation-crosslinked virgin and vitamin E-blended UHMWPEs were used as reference materials. The UHMWPEs were aged at 120 °C in air with oxidation levels analyzed by infrared spectroscopy. Tensile (n = 5 per group) and impact (n = 3 per group) properties before and after aging as per ASTM F2003 were evaluated. The wear rates were examined by pin-on-disc testing (n = 3 per group). The data were reported as mean ± SDs. Statistical analysis was performed by using Student's t-test for a two-tailed distribution with unequal variance for tensile and impact data obtained with n ≥ 3. A significant difference is defined with p < 0.05. The oxidation induction time of 100 kGy UHMWPE was prolonged to 144 hours with 0.05 wt% dodecyl gallate and 192 hours with 0.05 wt% gallic acid compared with 48 hours for 0.05 wt% vitamin E-blended UHMWPE. Accelerated aging of these polyphenol-blended UHMWPEs resulted in ultimate tensile strength of 50.4 ± 1.4 MPa and impact strength of 53 ± 5 kJ/m(2) for 100 kGy-irradiated UHMWPE with 0.05 wt% dodecyl gallate, for example, in comparison to 51.2 ± 0.7 MPa (p = 0.75) and 58 ± 5 kJ/m(2) (p = 0.29) before aging. The pin-on-disc wear rates of 100 kGy-irradiated UHMWPE with 0.05 wt% dodecyl gallate and 0.05 wt% gallic acid were 2.29 ± 0.31 and 1.65 ± 0.32 mg/million cycles, comparable to 1.68 ± 0.25 and 2.05 ± 0.22 mg/million cycles for 100 kGy-irradiated virgin and 0.05 wt% vitamin E-blended UHMWPE. Based on the sample numbers tested in this study, polyphenols appear to effectively enhance the oxidation stability without altering the mechanical properties or pin-on-disc wear rate of radiation-crosslinked UHMWPE. Crosslinked UHMWPE with natural polyphenols with improved oxidative stability and low wear may find clinical application in joint implants.