Abstract
In this work, the evolution of reacted phase assemblage and molecular structure of alkali-activated slag (AAS) exposed to atmospheric natural carbonation is studied. The hardened AAS pastes with various activator types (i.e., sodium hydroxide, sodium carbonate, sodium sulfate, potassium hydroxide, and potassium carbonate solutions) and cured under two temperature conditions (20 °C and 80 °C) are evaluated. The results show that natural carbonation leads to a strong decalcification and silicate polymerization of calcium-aluminosilicate-hydrate (C-A-S-H) and precipitation of various calcium carbonate polymorphs depending on activator composition. The sulfate-activated slag shows the poorest carbonation resistance likely due to its limited CO2 absorption capacity, manifested with the formation of calcium carbonate polymorphs, gypsum, gibbsite, and calcium-deficit aluminosilicate gels. While high-temperature curing tends to increase the crystallinity level of C-A-S-H, it has little effect on its carbonation resistance in terms of phase and molecular stability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.