Abstract
Transition metal dichalcogenide (TMD)-based coatings are known for their low friction performance, which is attributed to the formation of a tribolayer consisting almost exclusively of pure well-ordered TMD. However, the formation of such a tribolayer and its wear track coverage is still unknown. In this study, we employed surface mapping and nanotribological techniques to study the properties of the wear tracks of composite W-S-C coatings. Our analysis revealed that the as-deposited coating consisted of two phases, with significantly different nanoscale frictional properties. We attributed the phases to nanocrystalline WS2 (low friction) and amorphous solution of carbon and WS2 (high friction). The two phases wear at different rates, especially at lower loads, where we observed faster depletion of nanocrystalline WS2. In the wear track, sparse flat WS2 flakes were identified, suggesting that the recrystallization of the WS2 phase occurs only at the spots where the contact pressure is the highest.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.