Abstract
High coercivity, the highest for Cu-free 2 : 17 Sm-Co ribbons, has been obtained in as-spun (= 211 kOe) and short time annealed (= 232 kOe) samples of Sm(CobalFe Zr B)7 5 alloys, with varying B, Zr, and Fe content (= 0-0 06, = 0-0 16, = 0 08-0 3) and wheel speed. In as-spun samples, the TbCu7 type structure and in annealed samples the Th2Zn17 and CaCu5 type structures is observed, plus fcc Co as minority phase is observed. Reduced remanence () is higher than 0.7. High-temperature magnetic measurements show very good stability above 300 C with coercive field as high as 5.2 kOe at 330 C. For annealed Sm(CobalFe0 3Zr0 02B0 04)7 5, very good loop squareness and high maximum energy product of 10.7 MGOe have been obtained. Increasing Zr content results in less uniform microstructure of annealed ribbons.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.