Abstract
The microstructural and magnetic properties of Mn3Ga alloys with D022 phase have been investigated. Mn3Ga alloys with a nearly pure D022 phase were obtained via a heat treatment of ground arc-melted ingot powders with a cubic structure. X-ray difraction results show the formation of D022 after annealing the as-prepared ingot at 673 K for different annealing time intervals. It was found that the annealed samples are magnetically hard with a high HC of 11 kOe and a saturation magnetization of 20 emu g−1 at 300 K. Microstructure studies on the annealed powders showed the presence of small grains with size below 30 nm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.