Abstract
Nanosized tin dioxide samples (mean particle size: 3 nm, surface area: 170 m2 g−1) have been prepared and studied by UV–VIS–NIR diffuse reflectance spectroscopy, transmission electron microscopy, EPR and electrical conductivity measurements. The absorption threshold due to the SnO2 interband transition appears near 340 nm (3.6 eV) compared to about 1770 nm (0.7 eV) for orthorhombic SnO. When treated in reducing conditions (vacuum, hydrazine), SnO2 shows also a broad absorption in the visible range (350–600 nm) which disappears upon heating in oxygen. This broad absorption is also recorded upon direct heating in oxygen. This spectral feature is ascribed to the formation of oxygen vacancies, which depends on both oxygen pressure and temperature. The variation of electrical conductivity with oxygen pressure P, expressed by σ = k P−1/4, shows that singly ionized anionic vacancies are the main structure defects, in agreement with EPR measurements. An original method of preparation of colloidal SnO2 is also presented; the samples obtained show a still larger surface area (250 m2 g−1), a very narrow particle size distribution (1.1–2.4 nm), a high resistance to sintering and a low propensity to nonstoichiometry.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.