Abstract

The use of ordered catalyst layers, based on micro-/nanostructured arrays such as the ordered Nafion array, has demonstrated great potential in reducing catalyst loading and improving fuel cell performance. However, the size (diameter) of the basic unit of the most existing ordered Nafion arrays, such as Nafion pillar or cone, is typically limited to micron or submicron sizes. Such small sizes only provide a limited number of proton transfer channels and a small specific area for catalyst loading. In this work, the ordered Nafion array with a pillar diameter of only 40 nm (D40) was successfully prepared through optimization of the Nafion solvent, thermal annealing temperature, and stripping mode from the anode alumina oxide (AAO) template. The density of D40 is 2.7 × 1010 pillars/cm2, providing an abundance of proton transfer channels. Additionally, D40 has a specific area of up to 51.5 cm2/cm2, which offers a large area for catalyst loading. This, in turn, results in the interface between the catalyst layer and gas diffusion layer becoming closer. Consequently, the peak power densities of the fuel cells are 1.47 (array as anode) and 1.29 W/cm2 (array as cathode), which are 3.3 and 2.9 times of that without array, respectively. The catalyst loading is significantly reduced to 17.6 (array as anode) and 61.0 μg/cm2 (array as cathode). Thus, the nanosized Nafion array has been proven to have high fuel cell performance with low Pt catalyst loading. Moreover, this study also provides guidance for the design of a catalyst layer for water electrolysis and electrosynthesis.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.