Abstract
Nanosized hydoxyapatite (Ca10(PO4)6(OH)2 or HA) powders were prepared by a coprecipitation process using calcium nitrate and phosphoric acid as starting materials. The synthesized powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Brunauer-Emmett-Teller (BET) specific area measurment techniques. Single phase HA, with an average grain size of about 60 nm and a BET surface area of 62 m2/g, was obtained. No grain coarsening was observed when the HA powders were heated at 600°C for 4 hours. HA ceramics were obtained by sintering the powders at temperatures from 1000°C to 1200°C. Dense HA ceramics with a theoretical density of 98% and grain size of 6.5 μm were achieved after sintering the HA powders at 1200°C for 2 hours. HA phase was observed to decompose into tricalcium phosphate when sintered at 1300°C. The microstructure development of the sintered HA ceramics with sintering temperature was also characterized and discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.