Nanosecond pulsed laser damage characteristics of HfO_2/SiO_2 high reflection coatings irradiated from crystal-film interface

Abstract

The nano-precursors in the subsurface of Nd:YLF crystal were limiting factor that decreased the laser-induced damage threshold (LIDT) of HfO(2)/SiO(2) high reflection (HR) coatings irradiated from crystal-film interface. To investigate the contribution of electric-field (E-field) to laser damage originating from nano-precursors and then to probe the distribution of vulnerable nano-precursors in the direction of subsurface depth, two 1064 nm HfO(2)/SiO(2) HR coatings having different standing-wave (SW) E-field distributions in subsurface of Nd:YLF c5424181043036123rystal were designed and prepared. Artificial gold nano-particles were implanted into the crystal-film interface prior to deposition of HR coatings to study the damage behaviors in a more reliable way. The damage test results revealed that the SW E-field rather than the travelling-wave (TW) E-field contributed to laser damage. By comparing the SW E-field distributions and LIDTs of two HR coating designs, the most vulnerable nano-precursors were determined to be concentrated in a thin redeposition layer that is within 100 nm from the crystal-film interface.