Abstract
Polymer nanocomposites (pNC) have attracted wide interests in electrical insulation applications. Compared to neat matrices or microcomposites, pNC provide significant improvements in combined electrical, mechanical and thermal properties. In the understanding of the reasons behind these improvements, a major role was attributed to the interphase, the interaction zone between the nanoparticles (NP) and the matrix. Because of their nanoscale dimensions, the interphase properties are mostly theoretically described but rarely experimentally characterized. The aim of this study is to propose a nanoscale measurement protocol in order to probe mechanical (Young modulus) and electrical (dielectric permittivity) interphase features using, respectively, the peak force quantitative nanomechanical (PF-QNM) and the electrostatic force microscopy (EFM) modes of the atomic force microscopy. Measurements are performed on polyimide/silicon nitride (Si3N4) nanocomposite and the effect of a silane coupling agent treatment of Si3N4 NP is considered. In order to accurately probe mechanical properties in PF-QNM mode, the impacting parameters such as the applied force, the deformation and the topography are taken into account. The interphase region has shown a higher elastic modulus compared to the matrix and a higher width (W I) value for treated NP. From EFM measurements combined to a finite element model feeded with the W I values obtained from PF-QNM, the interphase permittivity is determined. The corresponding values are lower than the matrix one and similar for untreated and treated NP. This is in total agreement with its higher elastic modulus and implies that the interphase is a region around the NP where the polymer chains present a better organization and thus, a restricted mobility.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.