Abstract
Clusters based on the mixed-valence gigantic inorganic ring [Mo154O462H14(H2O)70]14- ({Mo154}-ring) and dimethyldioctadecylammonium (DODA) were combined to form novel molecular assemblies of an inorganic-organic hybrid molecular system as Langmuir-Blodgett (LB) and cast films. (DODA)20[Mo154O462H8(H2O)70] (2) was prepared by cation exchange and was characterized by a combination of thermogravimetry, IR, UV-vis-NIR, 1H NMR, and XRD measurements. The salt 2 was soluble in common organic solvents, and the chemical stability of {Mo154}-ring encapsulated by DODA cationic surfactants in CHCl3 was found to be higher than that of the "native" sodium salt of the {Mo154}-ring in H2O. Uniform spherical vesicle-like molecular assemblies of (DODA)20[Mo154O462H8(H2O)70] were observed in dilute THF, whose average diameter of 95 nm and a normalized variance of 5.7% were confirmed by a X-ray small-angle scattering. Deposition of 2 as a cast film showed circular domains with a typical diameter of approximately 100 nm, indicating possible similarities between solution and surface-deposited structures. The resulting LB films of salt 2 were transferred from an acidic buffer subphase with pH = 1.5 onto mica, giving a two-dimensional film surface with a unity transfer ratio. Further, the electronic absorption spectra of the LB multilayer were consistent with the classic type II mixed-valence MoV/MoVI electronic state well know for molybdenum blue {Mo154}-ring systems, and it appears that on the surface the plane of the {Mo154}-ring is approximately parallel to the substrate surface, as indicated by polarized electronic spectra, while the alkyl chains of DODA were relatively normal to the substrate surface. Therefore, the layer between the {Mo154}-rings and DODA cations was alternately stacked along the direction of film propagation. Finally, it was found that the surface morphology of the cast and LB films was determined by the molecular assembly of (DODA)20[Mo154O462H8(H2O)70] in solution and the air-water interface, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.