Abstract
PurposeThis study aims to evaluate the microtensile bond strength (µTBS) and failure modes of graphene nanoplatelets doped with hydroxyapatite (GNP-HA) modified self-etch dentin bonding agent (DBA) to caries effected dentin (CAD) after various conventional and laser disinfection protocols. Materials and MethodsGraphene nanoplatelets and HA nanoparticles were doped and incorporated in DBA. Fifty carious human molar teeth were used for the experiment. CAD specimens were divided into five groups (n=10/group) into CAD undergoing no disinfection treatment (Group-CAD), 2% chlorhexidine disinfection (Group-CHX), 6% NaOCl disinfection (Group-NaOCl), methylene blue assisted PDT (Group-MB-PDT), and Er,Cr:YSGG laser application (Group-Er,Cr:YSGG). Following the respective disinfection techniques, the GNP-HA modified adhesive was applied to all treated CAD surface. Subsequently µTBS and failure modes were analyzed. ResultsRepresentative scanning electron microscope images (SEM images) of the synthesized GNP-HA indicated flakes of graphene with varying size lengthwise (>500 nm) with 1-2 nm width. The doped HA showed round and spherical morphology conjugated over the surface of the GNP measuring 40 -100 nm in diameter. CAD group that underwent no treatment represented the highest µTBS (29.43 MPa). Within the tested specimens, MB-PDT (22.37 MPa) and Er,Cr:YSGG (21.85 MPa) showed the highest µTBS values than CHX (15.69 MPa) and NaOCl (11.46 MPa). However, there was no significant difference between MB-PDT and Er,Cr:YSGG (p>0.05) and a significant difference existed between CHX and NaOCl (p<0.05). Equal distribution of cohesive and adhesive failures was noted for CAD, CHX and NaOCl treated specimens. A majority of adhesive failures existed in the MB-PDT groups. While admixed and adhesive failures were higher in Er,Cr:YSGG treated samples. ConclusionsThe outcome of this study suggests that CAD restored by GNP-HA modified self-etch adhesive showed highest bond strength after MB-PDT and Er,Cr:YSGG protocols with low amount of adhesive failure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.