Nanometric Iridium Overlayer Catalysts for High-Turnover NH3 Oxidation with Suppressed N2O Formation

Abstract

In the present study, we prepared a 12 nm thick Ir overlayer via pulsed cathodic arc plasma deposition on a 50 μm thick Fe–Cr–Al metal (SUS) foil. Using this thin-film catalyst made NH3–O2 reactions more environmentally benign due to a much lower selectivity for undesirable N2O (<5%) than that of a Pt overlayer (∼70%) at 225 °C. Despite its small surface area, Ir/SUS exhibited promising activity as an ammonia slip catalyst according to a turnover frequency (TOF) >70-fold greater than that observed with conventional Ir nanoparticle catalysts supported on γ-Al2O3. We found that the high-TOF NH3 oxidation was associated with the stability of the metallic Ir surface against oxidation by excess O2 present in simulated diesel exhaust. Additionally, we found that the Ir overlayer structure was thermally unstable at reaction temperatures ≥400 °C and at which point the Ir surface coverage dropped significantly; however, thermal deterioration was substantially mitigated by inserting a 250 nm thick Zr buffer layer between the Ir overlayer and the SUS foil substrate (Ir/Zr/SUS). Although N2O formation was suppressed by NH3 oxidation over Ir/Zr/SUS, other undesired byproducts (i.e., NO and NO2) were readily converted to N2 by coupling with a V2O5–WO3/TiO2 catalyst in a second reactor for selective catalytic reduction by NH3. These results demonstrated that this tandem reactor configuration converted NH3 to N2 with nearly complete selectivity at a range of 200–600 °C in the presence of excess O2 (8%) and H2O (10%).