Abstract
The attempt to interpret the experimentally established regularities of strengthening surface nanostructures formation under different energy effects (electro-explosive alloying, electron-beam treatment, rolling products thermomechanical strengthening due to accelerated cooling, severe mechanical action at long term operation) was made on unified position. The mathematical modeling of nanostructured states formation in consideration of equilibrium states instabilities development in surface layers (Kelvin–Helmholtz and Marangoni instabilities) was carried out, the corresponding dispersion equations were analyzed and the analytical dependences of instability decrement α on perturbation wave length λ in micro and nanoranges were established. The correspondence of numerical values of maximum observed on the α(λ) dependences to experimental nanostructure parameters was noted and its physical interpretation was made.
Highlights
Gromov V.E. Formation of nanophases in electroexplosive alloying with aluminum and boron
Belov E.G., Efimov O.Y., Yur’ev A.B., Ivanov Y.F., Gromov V.E. Evolution of the structural-phase state of the surface of plasmahardened rollers // Steel in Translation
Summary
С единых позиций интерпретируются экспериментально установленные закономерности формирования упрочняющих поверхностных наноструктур при различных внешних энергетических воздействиях (электровзрывном легировании, электронно-пучковой обработке, термомеханическом упрочнении проката по режиму ускоренного охлаждения, интенсивных механических воздействиях при длительной эксплуатации рельсов). Формирование поверхностных наноструктур в материале при электронно-пучковой обработке Однако его анализ сопряжен со значительными трудностями, поэтому использовали дисперсионное уравнение для полубесконечного слоя: Формирование наноразмерных фаз при термомеханическом упрочнении проката
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have