Abstract
ABSTRACT In this work, nanoindentation on a (110) crystal plane with a spherical indenter and (111) twin boundaries at different distances was simulated using molecular dynamics. In addition, the load–displacement curves and mechanical properties were calculated, and the deformation mechanism of the nickel matrix was analysed using a dislocation extraction algorithm (DXA). The results showed that the load decreased in the load–displacement curve, which was caused by the initial nucleation of the dislocations, and the twinning boundary hindered dislocation propagation. Furthermore, Young’s modulus values near the twin boundary were lower than those farther away, and the maximum shear stress near the twin boundary was lower. Therefore, dislocation activity in the nickel matrix during indentation was mainly in the form of Shockley partial dislocations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.