Abstract
Amorphous alloy Fe68.5Co5Nb3Cu1Si15.5B7 was obtained by melt spinning. Samples cut from the foil were annealed at 450, 550, 650 and 750°C in a vacuum furnace. 57Fe Mossbauer spectroscopy was used to identify the crystalline phases formed and the orientation of the magnetic moments based on the refined values of the hyperfine parameters. The spectra of the samples annealed at 550, 650 and 750°C were indicative of nanocrystallization, with the magnetic moments reoriented out-of-plane for the last sample. This behavior is in contradistinction to that of the Co-rich system, which was totally crystallized at these annealing temperatures. Our results show that small Co additions can lead to the formation of nanostructures over a whole range of annealing temperatures. A new series of Mossbauer spectra was obtained by recording simultaneously the intensity transmitted by a superposition of the sample with the stainless steel etalon, based on the dual absorber method previously introduced by us. The values of the recoilless fraction could be derived from the relative spectral areas. The f factor maintained values close to 0.7 for all samples measured, but dropped to 0.37 for the sample annealed at 750°C. This behavior could be related to the presence of elastic stresses in the system, which caused the out-of-plane reorientation of the magnetic moment directions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.