Nanocrystalline WC-Co HVAF Coatings by Utilizing Novel Powder Manufacturing Route Using Water-Soluble Raw Materials

Abstract

In this study, nanostructured WC-Co coatings were produced using experimental nanocrystalline WC-12Co and WC-24Co powders produced by a novel chemical synthesis route. Test coatings were produced using HVAF spraying keeping the temperature as low as possible during the deposition in order to avoid decomposition of the nanocarbides. In experimental powders, two different Co incorporation methods were used: a conventional way in which cobalt was incorporated as a metallic Co powder and a chemical synthesis way in which cobalt acetate was used as a cobalt source. When using cobalt acetate, it decomposes to metallic cobalt during the process. Experimental powders in which cobalt acetate has been used as cobalt source resulted poor deposition efficiency. With warmer parameters, powders resulted better DE, but significant WC decarburization and the dissolution into the matrix phase occurred. Powders in which Co has been introduced as Co powder showed enhanced DE enabling spraying with decreased temperature and higher particle velocity, resulting in coatings with less WC decomposition. Especially, an experimental powder in which Co has been incorporated both as Co powder and as Co-Ac results very fine nanocarbide structure with significantly less WC decomposition having a hardness value of 1201 HV0.3, even with 24% Co.