Abstract
The binary nanocomposites blended by carboxymethyl cellulose (CMC) and SiO2 nanoparticles were constructed to prepare the films with superior thermal stability and flame retardant properties. The incorporation of cellulose nanofibers(CNFs) and SiO2 nanoparticles were followed to prepare ternary nanocomposite films exhibiting excellent mechanical properties. The mechanism and chemical reaction of the thermal decomposition for the CMC/SiO2 composite membrane were proposed, which showed that the mass residuals were Na2CO3, SiO2 and Na2SiO3, Na2CO3 when the content of the SiO2 nanoparticles was lowered and higher than 9.6 %, respectively. Compared with the pure CMC, micro combustion calorimeter (MCC) showed that the total heat release (THR) and the peak heat release rate (PHRR) both decreased from 6.4 kJ/g to 5.8 kJ/g, 134 w/g to 27 w/g, respectively. Moreover, mechanical properties of CMC/CNFs/SiO2 membrane showed that the toughness and rigidity of the nanocomposites increased by 56.0 % and 63.0 % on the basis of CMC, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.