Abstract
Fabrication of nanocomposite membranes with high nanoparticle loading is a significant challenge because of the serious agglomeration of nanoparticles at high concentration. In this study, poly(ethylene glycol)-functionalized polyoctahedral oligomeric silsesquioxanes (PEG@POSS) nanoparticles were incorporated into a sodium alginate (SA) matrix to fabricate nanocomposite membranes. A large loading of PEG@POSS up to 50wt% with a well dispersion in the membrane was achieved due to the good compatibility between PEG@POSS and alginate chains. Benefiting from the nanostructured size of PEG@POSS (1–3nm), the obtained nanocomposite membranes possessed very thin active layers of 180–200nm. A large quantity of hydrophilic PEG side chains enhanced the membrane surface hydrophilicity and offered massive water binding sites in the membranes. Homogeneously dispersed high content PEG@POSS nanoparticles increased the free volume of the nanocomposite membranes while maintaining a suitable free volume cavity size for water permeation. The optimum separation performance with a permeation flux of 2500gm−2h−1 and a separation factor of 1077 for dehydration of 90/10wt% ethanol/water feed was achieved. Additionally, the effects of operation temperature and feed concentration on separation performance were investigated systematically.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.