Abstract
Native oxide layer with thickness of about 1 nm was found easy to form on 6H-SiC surface during transporting from cleaning process to vacuum chambers, which was examined by x-ray photoelectron spectroscopy (XPS) and high-resolution transmission electron microscopy (HRTEM). The interface band bending was studied by synchrotron radiation photoelectron spectroscopy (SRPES). For the native-oxide/SiC surface, after Ni deposition, the binding energy of Si 2p red-shifted about 0.34 eV, which suggested the upward bending of the interface energy band. Therefore, the native oxide layer should be considered on the study of SiC devices because it may affect the electron transport properties significantly.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.