Nano-Columnar Mg Thin Films Created by Plasma Sputter Deposition for Improved Hydrogen Kinetics and Storage Properties

Abstract

ABSTRACTThe hydrogen storage properties of nanostructured Mg and MgH2 thin films were studied as created by Ar and Ar+H2 plasma sputter deposition. Columnar structures with typical widths of ∼120 nm are observed with their long columnar axis extending throughout the thickness of the films. Applying substrate bias voltages during deposition results in narrower columns. A concomitant reduction in hydrogen desorption temperature from 400 °C to 360 °C is observed. Capping the Mg films with a ∼100 nm thin Pd layer leads to significantly reduced hydrogen desorption temperatures of ∼200 °C induced by the catalytic activity of the Pd cap layer. Also, hydrogen permeation of the films is strongly improved. The rate-determining factor is found to be the dissociation of the hydrogen molecules. Optimum hydrogen loading conditions of the Pd/Mg films were obtained just above ∼200 °C at hydrogen pressures of 0.25–1.0 MPa, resulting in hydrogen storage capacities in the range of 4–7 wt%.