An experimental study of oxidation of nano aluminum (Al) powders in CO2 and O2 is described. The oxidation is studied using thermogravimetric (TG) measurements from room temperature to 1500°C. Partially oxidized samples are recovered and their compositions are analyzed using X-ray diffraction. The oxidation product morphology was examined using SEM. Dimensional properties of aluminum particles have a significant influence on the oxidation processes. The nano aluminum reaction onset temperature was much lower than micro aluminum. Distinctly different oxidation properties of nano aluminum powders were shown between CO2 and O2. nano aluminum powders could ignite in O2 at fairly low temperatures around 530 °C. However ignition for nano aluminum powders in CO2 didn't appeared below 1500 °C. There was a weight loss in the TG curves at around 1200 °C for nano Al-CO2 system. It was thought that small amount of carbon formed in the oxidation process. The XRD showed that both the nano aluminum oxidation products were α-Al2O3 in CO2 and O2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have