Abstract
Plasma-carburizing treatment of powder metallurgy chromium was carried out and the following results were obtained.1) X-ray diffraction analysis showed the formation of Cr3C2, Cr7C3 and Cr23C6.2) Cr23C6 was formed in the surface at the early stages of the carburizing process, but Cr7C3 and Cr3C2 were formed as treatment proceeded.3) The thickness of the carbide layer was proportional to the square root of treatment time
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.