Abstract

The corrosion resistance of implant alloys was investigated by anodic polarization measurements in pseudo physiological solution. Role of alloying elements in passive film formed on implant alloys by the anodic polarization was also examined with X-ray photoelectron spectroscopy (XPS). Passivity zones of SUS316L stainless steel and Co-Cr alloys are narrow, and a rapid increase of current density results from the low potential in comparison to Ti alloys. The passive current density of Ti-15%Zr-4%Nb-2%Ta-0.2%Pd alloy (mass%) is very low. Effects of protein and dissolved oxygen with 90%N2+5%CO2+5%O2 gas bubbling on anodic polarization curves are not detected. The passive film formed on the Ti-6%Al-4%V extra low interstitial alloy consist mainly of TiO2, Al2O3 and small amounts of V oxide. Passive films on Ti-15%Zr-4%Nb-2%Ta-0.2%Pd and Ti-15%Sn-4%Nb-2%Ta-0.2%Pd alloys consist of TiO2, ZrO2, SnO2, Nb2O5, Ta2O5 and PdO or Pd. XPS spectra from the Co-Cr alloy and SUS316L stainless steel show peaks of Cr2O3, CoO, Fe oxide, Mo oxide, Ni, Co, Fe, Mo and Cr. As Ni, V and Co are strong cytotoxic elements, it was found that biocompatibility of SUS316L, Co-Cr, Ti-6%Al-4%V ELI alloys become lesser after a long time use in the living body. The thickness of the passive film on Ti alloys is thinner than that of Co-Cr alloy. Passive film formed on Ti-15%Zr-4%Nb-2%Ta-0.2%Pd alloy is strong and stable.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.