AbstractRecently, stress corrosion cracking (SCC) has been observed near the welded zone of the primary loop recirculation pipes made of low-carbon austenitic stainless steel type 316L in boiling water reactors. SCC is initiated by superposition effect of three factors. They are material, environmental and mechanical factors. For non-sensitized material such as type 316L, residual stress as a mechanical factor of SCC is comparatively important. In the joining processes of pipes, butt welding is conducted after surface machining. Surface machining is performed in order to match the inside diameter and smooth surface finish of pipes. Residual stress is generated by both processes. Moreover, residual stress distribution generated by surface machining is varied by subsequent welding processes, and it has the maximum residual stress around 900 MPa near the weld metal. The variation of metallographic structure, such as recovery and recrystallization, in the surface machined layer due to the welding thermal cycl...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.