Abstract
In this study, Fatigue Strength of Hot Work Tool Steel SKD61 was investigated. Development of new-style hot work tool steel of SKD61 is advanced at present. Data about the fatigue strength which changed the training ratio of hot work tool steel are poor. A static bending test and fatigue test were curried out an examination sequentially to make fatigue strength clear and investigated it for the observation of the fracture surface using SEM and EDX. In the case of a training ratio change, it was found that static bending strength of K materials was same as that of reference materials. K materials had lower fatigue strength than reference materials over a range of number of cycles from 104 to 107. As a result of fracture observation, the fracture origin was aluminum and oxygen mainly. Because alumina (Al2O3) to use at the time of deoxidation as a probable cause remains behind, it becomes the destruction fracture origin.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: The Proceedings of Mechanical Engineering Congress, Japan
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.