Multi-scale investigation of microstructure, fiber pullout behavior, and mechanical properties of ultra-high performance concrete with nano-CaCO3 particles

Abstract

The mechanical properties of a fiber-reinforced concrete are closely related to the properties of the matrix, fiber, and fiber-matrix interface. The fiber-matrix bond property is mainly governed by the adhesion between the fiber and surrounding cement materials, as well as the strength of materials at the interfacial transition zone. In this paper, the effect of nano-CaCO3 content, varying between 0 and 6.4%, by mass of cementitious materials, on microstructure development, fiber-matrix interfacial bond properties, and mechanical properties of ultra-high performance concrete (UHPC) reinforced with 2% steel fibers were investigated. The bond properties, including bond strength and pullout energy, were evaluated. Mercury intrusion porosimetry (MIP), backscattered electron microscopy (BSEM), optical microscopy, and micro-hardness testing were used to characterize the microstructure of matrix and/or interfacial transition zone (ITZ) around an embedded steel fiber. Test results indicated that the incorporation of 3.2% nano-CaCO3 significantly improved the fiber-matrix bond properties and the flexural properties of UHPC. This was attributed to densification and strength enhancement of ITZ as observed from micro-structural analyses. Beyond the nano-CaCO3 content of 3.2%, the fiber bond and mechanical properties of UHPC decreased due to increased porosity associated with agglomeration of the nano-CaCO3.