Abstract
Polymers having high filler loading levels are not able to meet the increasing requirements of thermal interface materials by themselves; therefore, fillers and structures with unique advantages have been developed. In this study, mechanical mixing was used to disperse graphene nanoplatelets (GNPs) and boron nitride (BN) fillers inside thermoplastic polyurethane (TPU)-based films, which were then compounded into a multilayered structure. The multilayered BN-GNP/TPU composite film created during this study exhibited a high thermal conductivity of 6.86 W m−1 K−1 at a low filler loading of 20 wt% BN with 20 wt% GNP, which was significantly higher (2844%) than that of the neat TPU film. The composite film also had good durability to flexural fatigue and laundering. This was exhibited by maintaining thermal conductivity values of 6.25 W m−1 K−1 after 5000 cycles of the flexural fatigue test, and 6.85 W m−1 K−1 after 10 cycles of laundering, respectively. Furthermore, enhanced thermal stability, cooling, and hydrophobic properties of the multilayered BN-GNP/TPU composite films were also observed with the resulting composite film. Overall, such a system provides a facile approach that is applicable for the fabrication of multifunctional materials as thermal interface materials within smart cooling garments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.