Abstract

The development and application of additive manufacturing (AM) technologies is constantly increasing. However, in many applications, AM parts are subjected to multiaxial loads, arising from operating conditions and/or complex geometries. These make AM components serious candidates for crack initiation and propagation mechanisms. Therefore, a deep understanding of the multiaxial fatigue behavior of AM parts is essential in many applications where durability and reliability are core issues. In this study, multiaxial fatigue of Ti6Al4V thin-walled tubular specimens, made by Selective Laser Melting (SLM) process, was investigated by combined axial-torsional loads. Infrared thermography (IR) was also used to investigate the temperature evolution during fatigue tests. Results highlighted different damage mechanisms and failure modes in the low- and high-cycle fatigue regimes.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.