Abstract
This paper presents a method to investigate the behaviour of polymers on different scales during deformation using simultaneously collected synchrotron X-ray scattering, digital image correlation (DIC) and tensile loading. The method is demonstrated through experiments made on specimens of amorphous polycarbonate. Deformation is measured in-situ, simultaneously across different scales from the macroscopic deformation, measured using sensors on the tensile machine, to the full-field mesoscopic deformation, measured using DIC, down to the deformation of the nano-scale structure, studied using small and wide angle X-ray scattering (SAXS/WAXS). The DIC reveals highly inhomogeneous deformations that render conventional techniques for measuring deformation, such as extensiometers, virtually useless. The X-ray scattering is measured in several spatial points during continuous loading giving the evolution of the microstructure with respect to both spatial location and load level. The spatial mapping of the scattering reveals characters that would not be observed when only measuring at the centre point or measuring on a large area of the specimen, e.g. wide beam SAXS/WAXS or small angle neutron scattering (SANS). With these data, the macroscopic and the mesoscopic deformation can be correlated to the behaviour of the microstructure providing relevant information when developing micro-mechanical based constitutive models. The experimental results shown here indicate a direct correlation between the major principal strain direction and the maximum anisotropy direction of the SAXS patterns. The current approach can be extended to any kind of polymeric materials or polymer-based nano-composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.