Abstract
Dispersion of mixed suspensions of zircon and α -alumina using citric acid as dispersant followed by pressure filtration produced after sintering (1600∘C—2 h) dense mullite-zirconia composites. The effect of citric acid addition and pH on the rheological behavior of the mixed suspensions (57 vol%) was examined. Most of flow curves showed a shear thinning behavior at low shear rates reaching the viscosity a plateau at high shear rates. Newtonian viscosity at high shear rates values decreased to a minimum and then increased with increasing the amount of dispersant added. Compacts prepared from well stabilized suspensions achieved a maximum relative density of 72% (theoretical) which is slightly higher than that obtained from suspensions dispersed with a polyelectrolyte. Characteristics of sintered compacts such as density and crystalline phase composition by XRD were determined.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.