Abstract
Heat treatment of barium iron vanadate glass, BaO‐Fe2O3‐V2O5, at temperatures higher than crystallization temperature causes a marked decrease in resistivity (ρ) from several MΩcm to several Ωcm. 57Fe Mössbauer spectrum of heat-treated vanadate glass shows a marked decrease in quadrupole splitting (Δ) of FeIII, reflecting a structural relaxation, i.e., an increased symmetry of "distorted" FeO4 and VO4 tetrahedra which are connected to each other by sharing corner oxygen atoms. Structural relaxation of 3D-network of vanadate glass accompanies a decrease in the activation energy for the conduction, reflecting a decreased energy gap between the donor level and conduction band. A marked increase in the conductivity was observed in CuO- or Cu2O-containing barium iron vanadate glass after heat treatment at 450 °C for 30 min or more. "n-type semiconductor model combined with small polaron hopping theory" was proposed in order to explain the high conductivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.