Abstract
A polycrystalline BaCoZnFeSUB16/SUBOSUB27/SUB sample was prepared by the solid-state reaction method and wet ball-milling. The refined X-ray diffraction patterns revealed that the prepared sample was hexagonal with the space group P63/mm. To determine the spin transition temperature (TSUBS/SUB), the temperature dependence of the zero-field-cooled magnetization curves were measured under applied fields of 100 to 1000 Oe at various temperatures ranging from 4.2 to 295 K. TSUBS/SUB is the temperature at which the spin changes from the planar to the conical direction at the 135 K. From the hysteresis curves at various temperatures ranging from 4.2 to 295 K, the coercivity showed a change in slope at TSUBS/SUB. Mössbauer spectra were obtained at various temperatures ranging from 4.2 to 295 K, and the magnetic hyperfine field and electric quadrupole splitting of the sample showed abrupt changes around TSUBS/SUB.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call