Abstract
Due to the "shuttle effect" and low conversion kinetics of polysulfides, the cycle stability of lithium sulfur (Li-S) battery is unsatisfactory, which hinders its practical application. The Mott-Schottky heterostructures for Li-S batteries not only provide more catalytic/adsorption active sites, but also facilitate electrons transport by a built-in electric field, which are both beneficial for polysulfides conversion and long-term cycle stability. Here, MXene@WS2 heterostructure was constructed by in-situ hydrothermal growth for separator modification. In-depth ultraviolet photoelectron spectroscopy and ultraviolet visible diffuse reflectance spectroscopy analysis reveals that there is an energy band difference between MXene and WS2 , confirming the heterostructure nature of MXene@WS2 . DFT calculations indicate that the Mott-Schottky MXene@WS2 heterostructure can effectively promote electron transfer, improve the multi-step cathodic reaction kinetics, and further enhance polysulfides conversion. The built-in electric field of the heterostructure plays an important role in reducing the energy barrier of polysulfides conversion. Thermodynamic studies reveal the best stability of MXene@WS2 during polysulfides adsorption. As a result, the Li-S battery with MXene@WS2 modified separator exhibits high specific capacity (1613.7 mAh g-1 at 0.1 C) and excellent cycling stability (2000 cycles with 0.0286 % decay per cycle at 2 C). Even at a high sulfur loading of 6.3 mg cm-2 , the specific capacity could be retained by 60.0 % after 240 cycles at 0.3 C. This work provides deep structural and thermodynamic insights into MXene@WS2 heterostructure and its promising prospect of application in high performance Li-S batteries.
Published Version (Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.