Abstract
In this work, an electrodeposited superhydrophobic nickel film with apparent contact angle of 156° was fabricated using different contents of H3BO3 as a morphological modifier to effectively improve the corrosion resistance of the underlying copper substrate. Atomic force microscopy and scanning electron microscopy analysis allowed visualization of growth mechanism and morphology of the electrodeposited coating in the presence and absence of H3BO3. The results showed that H3BO3 considerably effects on morphology of coating by its hindering property that leads to form micro and micro-nanocones hierarchical structures with the mechanism of screw dislocation-driven growth. The spontaneous adsorption of airborne hydrocarbon contaminants on the nickel micro-nanostructures enhances the hydrophobicity of the surface. Cyclic voltammetry and X-ray diffraction provide other evidences of the boric acid hindering effect. The quantitative analysis of atomic force microscopy results showed that after about 5 months exposure to air, the roughness value has been decreased and apparent contact angle has been decreased to 127°. Finally, corrosion behavior of the superhydrophobic nickel film was investigated in 3.5 wt.% NaCl by means of AC/DC electrochemical methods. Regarding potentiodynamic polarization and electrochemical impedance spectroscopy, the superhydrophobic nickel film (Cassie-Baxter state) exhibited five times greater corrosion resistance in comparison with fresh nickel film (Wenzel state).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Colloids and Surfaces A: Physicochemical and Engineering Aspects
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.