ABSTRACTSilicon nitride (Si3N4) has excellent thermo-mechanical properties, and can be used as heat dissipation substrate for various devices. Si3N4 thin films are generally synthesised by chemical vapour deposition (CVD) or plasma-enhanced CVD. The use of polysilazanes (PSZs) as a precursor to the synthesis of Si3N4 has attracted significant attention because of their high mouldability and processability. In this study, Si3N4 thick films were prepared on silicon wafers or aluminium substrates by a spin- or dip-coating liquid PSZ, followed by UV curing and IR heat treatment under various conditions. The effects of the heat treatment conditions on the Si3N4 thick film surface were analysed by optical microscopy, X-ray diffraction, and scanning electron microscopy. An almost single phase of Si3N4 was synthesised successfully on the single crystalline silicon with UV curing at 400°C for 30 min and IR heating at 800°C in N2 atmosphere.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.