Abstract
Thin films of an asymmetric styrene-block-ferrocenyldimethylsilane copolymer were studied on solid silicon substrates as well as free-standing. In the bulk the diblock forms poly(ferrocenylsilane) cylinders in a poly(styrene) matrix. The thin films were analyzed by a variety of techniques including atomic force microscopy (AFM), transmission electron microscopy (TEM), X-ray reflectivity, secondary ion mass spectrometry (SIMS), and optical microscopy. From X-ray reflectivity measurements it was concluded that both blocks were press nt at the substrate, whereas poly(styrene) wetted the free surface. The formation of islands and holes was observed by optical microscopy and AFM, as a result of a mismatch between the film thickness and the eqt ilibrium spacing between layers of cylinders. Upon longer annealing of the films, the islands disappeared iue to a change of the internal morphology of the thin film. After selective removal of the organic matrix by means of oxygen reactive ion etching, the phase-separated structure could be visualized by AFM. The morphology of the films altered upon annealing from an inplane cylindrical to a hexagonal morphology. The structure in free-standing films could be analyzed by TEM. After annealing, both types of orientations of cylinders (parallel and perpendicular with respect to the surface) were found to be stable.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.