Abstract
A melt‐extruded method has been used to prepare blend membranes of Perfluorosulfonic Acid Polymer (PFSA) and Perfluorocarboxylic Acid Polymer (PFCA) with different combination ratios. Fourier Transform Infrared (FT‐IR) and X‐ray Diffraction (XRD) analyses have showed that the chemical structure and crystallization behaviour of both polymers remained unchanged in the blend membrane, and the crystallinity has been increased for the blend membrane with a higher weight fraction of PFCA. According to the results obtained from Scanning Electron Microscope (SEM), PFSA and PFCA polymers are well compatible, forming mixed aggregates containing both sulphonyl and carboxyl ions. Surprisingly, a membrane containing a 50:50 ratio of PFSA/PFCA has showed microphase separation, and it possesses the smallest ionic cluster size among all the blend membranes prepared, as illustrated by the Small Angle X‐ Ray Scattering (SAXS) analysis. In addition, when the PFCA content was increased, the ion exchange capacity (IEC) for blend membranes remained the same, while their water uptake and proton conductivity have decreased rapidly. Compared with the PFSA/PFCA two‐layered membrane, this PFSA/blend/PFCA membrane not only maintained respectable electrolysis property, also exhibited significantly higher peel strength, especially after the hydrolization process; plus, it has showed excellent resistance to the peeling damage under the operational conditions of chlor‐alkali electrolytic cells. POLYM. ENG. SCI., 55:180–189, 2015. © 2014 Society of Plastics Engineers
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.