Morphology and kinetics of nanoheterogeneities in Fe81Ga19–Tb alloy: A small-angle neutron scattering study

Abstract

The formation of nanoprecipitates in the Fe81Ga19 alloy doped with Tb (∼0.1 at. %) was studied by small-angle neutron scattering (SANS). Measurements at room temperature for several samples pre-aged at a fixed temperature in the range of (300–700)°C revealed a dilute system of precipitates with a characteristic size at nanoscale (<1000 Å) growing with an increase in ageing temperature. In situ measurements during isothermal ageing at 300 °C for 3 h revealed fast (order of 10 min) formation of precipitates. SANS analysis is consistent with the results of neutron diffraction experiments, which suggest the microstructure of this alloy as a matrix of disordered atomic structure (A2 phase) with embedded precipitates of the structurally and magnetically ordered D03 phase.