Abstract
Novel thermosetting poly[oligo(ethylene glycol) diacrylate]-sodium montmorillonite nanocomposites containing a range of clay volume fractions were prepared by an in situ polymerization method. X-ray diffraction showed that the basal plane spacing of the clay was increased to approximately 1.7 nm regardless of clay volume fraction. Transmission electron microscopy confirmed the basal spacing and intercalated structure. The elastic moduli of the composites were measured using ultrasonic pulse-echo equipment. The results show that the Young's modulus and shear modulus increase with nominal clay volume fraction up to 0.22, and are in good agreement with the well-established Christensen method and derived Hashin–Shtrikman bounds for conventional composites provided that the true volume fraction of clay reinforcement filler is calculated. At low clay volume fractions, the composites were transparent. When the nominal clay volume fraction was further increased, cracks and porous surfaces appeared, as observed by scanning electron microscopy. These defects decreased the elastic modulus, indicating an upper limit for clay additions in this preparation route. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 1785–1793, 2005
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.