Abstract
YSZ film was fabricated by a facile electrophoretic deposition process using commercial YSZ powders. YSZ films with average thickness of around 10 µm were deposited on LSM/YSZ substrate at 20 V for 20 minutes and subsequently sintered at 1200 °C, 1300 °C, and 1350°C. XRD patterns of the deposited and sintered films can be attributed to mostly cubic YSZ phase. On the other hand, SEM images revealed that a sintering temperature above 1300 °C was needed to obtain a denser YSZ film. The film morphology also showed that as the sintering temperature increases, the YSZ grain size also increases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.