Abstract
Nd1(Fe)0.2Ba1.8Cu3O7-δ oxide material have been successfully synthesized by solid-state reaction with modified heat treatment process to improve the heat time efficiency, calcination at 950°C for six hours, sintering at 975°C fo six hours, and annealing at 450°C for six hours, respectively. The X-ray diffraction pattern shows that a single-phase form of Nd1(Fe)0.2Ba1.8Cu3O7-δ is an orthorhombic (Pmmm) structure. The Rietveld refinement analysis found, the lattice parameter are a = 3.8758Å, b = 3.9101Å, and c = 11.7190Å with χ2 = 1.394%. The SEM-EDAX image shows that the samples are form clusters with size estimates of 10 - 40μm, and the elemental composition of the oxide materials is Ba rich.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.