Abstract
AbstractThe morphological transformation of expanded vermiculite (VC) during injection molding with brittle PLA and ductile PP polymers along with its positive and negative contribution to mechanical response is investigated. Polymer/VC mixtures with 30 wt. % VC are prepared by thermokinetic high shear mixing at 4000 rpm without any ex‐situ exfoliation agents or compatibilizers. Obtained composite mixtures are then injection molded onto three‐point bending and tensile test specimens. Performed mechanical tests suggested a significant increase in tensile (110%) and flexural modulus (112%) of PP30VC samples. Presented fractographic and morphological investigations suggested that the root cause of measured improved tensile (36%) and bending strength (26%) of PP is the fibrillation of VC associated with PP/VC interactions under high shear. A similarly increasing trend for tensile (147%) and bending modulus (137%) was observed for PLA30VC samples. Contrary to PP30VC, a decreasing pattern was present in the case of tensile (−40%) and bending strength (−13%) of PLA30VC. The root cause for such reduction is determined to be (i) in situ exfoliation of VC inside PLA matrix and transformation of VC into micrometer‐sized platelets; (ii) evaporation of trapped water/crystalline water in the interlayer region of VC which caused in situ degradation of PLA during manufacturing.Highlights Vermiculite‐loaded PP and PLA composites are produced at high shear. Composites have superior modulus compared to neat polymers. Fibrillation of platelet vermiculite is observed in only the PP matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.