Abstract
Grain boundary character distribution in equal-channel-angular pressed Zr was studied. Using a die design of 90°/20° and an operation temperature of 350°C. The initial grain size of 20 μm was reduced to about 270 nm with 4 passes via route Bc. The grain growth kinetics of the recrystallized state was obtained by experiment and Monte-Carlo computer simulation, respectively, which showed good agreement. Based on kinetics and morphological characteristics, it was concluded that the grain coarsening mechanism was governed by normal grain growth. No sign of abnormal grain growth was detected either in the experiment or in simulation despite taking into consideration anisotropy in grain boundary energy as well as its mobility. This indicates that grain boundaries produced by severely deformed Zr are stable against explosive coarsening. The evolution characteristics of the microstructure in the present ECA pressed and recrystallized Zr differed from those of cold rolled Ti in that the grain boundary misorientation distribution and texture were rather stable during grain growth.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.